Effect of Si and Holding Time on Ti2Al20La Phase in Al-Ti-La Intermediate Alloy
Hu Da, Xudong Tian, Jiazhi An, Wanwu Ding, Jianchao Chen, Haicun Yu, Haixia Zhang
TL;DR
This paper studies how adding silicon and varying holding time affects the Ti2Al20La phase in an aluminum-titanium-lanthanum alloy.
Contribution
The study reveals how Si and holding time alter the Ti2Al20La phase's content, shape, and structure in Al-Ti-La alloys.
Findings
Adding 2.3 wt.% Si reduces Ti2Al20La phase volume fraction from 21% to 4% and aspect ratio from 2.3 to 2.0.
With increased holding time, Ti2Al20La phase content and size decrease, while La-Si binary phase content increases.
Al11La3 dissolves and disappears as holding time increases.
Abstract
The effects of holding time and Si on the content, shape size and structure of Ti2Al20La phase in Al-Ti-La intermediate alloy were investigated by an X-ray diffractometer, scanning electron microscope and transmission electron microscope. The results show that the volume fraction and aspect ratio of Ti2Al20La phase in Al-Ti-La intermediate alloy decrease significantly, from 21% and 2.3 without Si addition to 4% and 2.0 with the addition of 2.3 wt.% Si at a holding time of 15 min at 750 °C, respectively. The Si element will attach to the Ti2Al20La phase and form La-Si binary phase at the grain boundary of α-Al. With the increase of holding time from 15 min to 60 min, the content of Ti2Al20La phase in the alloy gradually decreases and the size decreases significantly. Meanwhile, Al11La3 will dissolve and disappear, while the content of La-Si binary phase increases, and part of Ti2Al20La…
Genes, proteins, chemicals, diseases, species, mutations and cell lines named across the full text — each resolved to its canonical identifier and authoritative record.
Click any figure to enlarge with its caption.
Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10
Figure 11
Figure 12
Figure 13
Figure 14Peer Reviews
No public reviews on file for this paper yet. If you reviewed it on a platform where reviews are public (OpenReview, ICLR, NeurIPS, ICML), you can paste yours below so the community can read it here.
Videos
No videos yet. Explain this paper in a talk, walkthrough, or lecture? Add one.
Taxonomy
TopicsAluminum Alloy Microstructure Properties · Intermetallics and Advanced Alloy Properties · Titanium Alloys Microstructure and Properties