# Microstructure Evolution and Mechanical Properties of 7A52 Aluminum Alloy Thin Sheet Repaired with Friction Stir Surfacing

## TL;DR

A friction welding technique is used to repair aluminum alloy sheets, significantly improving their strength and mechanical properties.

## Contribution

The study demonstrates a solid-state repair method that enhances the mechanical properties of 7A52 aluminum alloy through microstructure evolution.

## Key findings

- The repair technique increases yield and tensile strength by up to 157.9% and 129.7% along the repair direction.
- Dynamic recrystallization and phase transformation contribute to the improved mechanical properties.
- Fracture occurs at the junction of the nugget zone and heat-affected zone due to texture differences and stress concentration.

## Abstract

A solid-state repair technique based on surface friction welding is investigated in depth to achieve excellent mechanical properties of damaged 7A52 aluminum alloy. The results show that the yield strength and tensile strength along the repair direction are 436 MPa and 502 MPa, respectively, at a rotational speed of 1400 rpm and a travel speed of 300 mm/min, which are about 157.9% and 129.7% of those before the defects were repaired, respectively, while the elongation is 17.2% compared to the base material. Perpendicular to the repair direction, the yield strength and tensile strength are 254 MPa and 432 MPa, which are 111.4% and 129.7% of those before the defects were repaired, respectively, while the elongation is 11.8% compared to the base material. The mechanical properties of the repaired areas are still improved compared to those of the defect-free sheets. On the one hand, this is attributed to the dynamic recrystallization of the nugget zone due to the thermo-mechanical coupling, resulting in the formation of a fine, equiaxed grain structure; on the other hand, the precipitated Mg2Si phase, which is incoherent within the base material, transforms into the Al12(Fe, Mn)3Si phase, as well as the precipitation of the Al6Mn phase and η′ phase, resulting in the enhancement of the properties. The material fracture at the junction of the nugget zone and the heat-affected zone occurs after repair, which is attributed to the significant difference in the texture of the nugget zone and the heat-affected zone, as well as to the stress concentration at the junction.