Photo-Assisted Pd-Nb2O5/Carbon Nanocomposites for Enhanced Ethanol Electro-Oxidation Kinetics and CO Tolerance in Alkaline Media

TL;DR

This study develops Pd-Nb2O5/C nanocomposites that significantly enhance ethanol electrooxidation kinetics, CO tolerance, and stability under light, advancing catalyst design for alkaline fuel cells.

Contribution

The paper introduces a novel photo-assisted Pd-Nb2O5/C nanocomposite catalyst with improved performance and durability for ethanol oxidation in alkaline media.

Findings

Pd-Nb2O5/C reduces ethanol oxidation onset potential by up to 160 mV.

Poisoning tolerance increases fivefold at fixed potential.

Light irradiation doubles the current density and improves catalyst stability.

Abstract

Pd-based anodes for alcohol oxidation suffer from surface poisoning and sluggish kinetics. Here, we developed Pd-Nb2O5/C nanocomposites to improve ethanol electrooxidation kinetics and CO tolerance in alkaline media. Orthorhombic Nb2O5 prepared by the Pechini route was combined with fcc Pd nanoparticles via polyol reduction, yielding Pd(x)-Nb2O5(y)/C nanocomposites with x:y = 100:0, 70:30, 50:50, 30:70, 0:100. Rietveld-refined X-ray diffraction confirmed phase purity and showed similar Pd crystallite sizes (4.46 nm for Pd/C and 4.92-5.08 nm for Nb2O5-containing catalysts). Transmission and scanning electron microscopies coupled with energy-dispersive X-ray spectroscopy reveal uniformly dispersed Pd nanoparticles on Nb2O5 and carbon. UV-Vis diffuse reflectance indicated a band gap of 3.10 eV, and chopped-light photocurrent measurements confirm the strong ultraviolet responsiveness of Nb2O5. X-ray photoelectron spectroscopy reveals that Pd(0.5)Nb2O5(0.5)/C had the highest Pd0 content (58.99%). Electrochemical testing demonstrates that, relative to Pd/C, optimized Pd(0.5)Nb2O5(0.5)/C reduces the ethanol oxidation onset potential by up to 160 mV, increases poisoning tolerance by a factor of five at a fixed potential, and raises the current density from 1.59 to 1.76 mA cm-2. Under light irradiation, the current density increases from 1.07 to 2.10 mA cm-2, accompanied by improved stability and extended durability, attributed to light-induced electron-hole generation and enhanced OH- adsorption. These results highlight the synergistic contribution of oxide-metal interactions and photoactivation to ethanol oxidation and provide insights for designing efficient catalysts for alkaline fuel cells. s