Metallicity without quasi-particles in room-temperature strontium titanate

TL;DR

This paper reveals that strontium titanate exhibits strange metallic behavior at room temperature, with resistivity exceeding the Mott-Ioffe-Regel limit, and proposes a novel interpretation involving Landauer transmission and polarons.

Contribution

It introduces the concept of metallicity without quasi-particles in strontium titanate and links resistivity behavior to Landauer transmission and large polarons, challenging existing theories.

Findings

Resistivity follows T^3 behavior above 100K and T^2 at low temperatures.

Resistivity exceeds the Mott-Ioffe-Regel limit, indicating strange metallicity.

A scaling relationship connects mobility, permittivity, and soft mode frequency.

Abstract

Cooling oxygen-deficient strontium titanate to liquid-helium temperature leads to a decrease in its electrical resistivity by several orders of magnitude. The temperature dependence of resistivity follows a rough T$^{3}$ behavior before becoming T$^{2}$ in the low-temperature limit, as expected in a Fermi liquid. Here, we show that the roughly cubic resistivity above 100K corresponds to a regime where the quasi-particle mean-free-path is shorter than the electron wave-length and the interatomic distance. These criteria define the Mott-Ioffe-Regel limit. Exceeding this limit is the hallmark of strange metallicity, which occurs in strontium titanate well below room temperature, in contrast to other perovskytes. We argue that the T$^{3}$-resistivity cannot be accounted for by electron-phonon scattering \`{a} la Bloch-Gruneisen and consider an alternative scheme based on Landauer transmission between individual dopants hosting large polarons. We find a scaling relationship between the carrier mobility, the electric permittivity and the frequency of transverse optical soft mode in this temperature range. Providing an account of this observation emerges as a challenge to theory.

Tables

Table 1. Table 1: How the MIR limit of metallicity is exceeded in different perovskytes- The table compares the Fermi wave-vector, the resistivity and the mean-free-path at 400 K in four different systems using equation 1. The table lists an underdoped, an optially-doped cuprate and strontium ruthenate and compares them with doped strontium titanate. In the case of YBa 2 Cu 4 O 8 , we assume that there are four Fermi surface pockets with a k F corresponding to the square root of the frequency of quantum oscillations. In contrast to other systems, the MIR limit in doped strontium titanate occurs well below room temperature.

Compound	kF (nm-1)	$\rho$(400K) (m$\Omega$cm)	$\ell$(400K)(nm)	kF$\ell$ (400K)	T${}_{k_F\ell =1}$ (K)	Reference
La1.72Sr0.18Cu04	6.6	0.32	0.35	2.2	850	Takagi:1992 ; Gunnarsson:2003
YBa2Cu4O8	1.4	0.36	0.8	1.1	450	Hussey:1997 ; Bangura:2008
Sr2RuO4	5.6	0.2	0.38	2.1	800	Tyler:1998
SrTiO3-δ (n=4 1017 cm-3)	0.24	5900	0.2	0.05	100	This work

Equations

$$\sigma =\frac{n{e}^2\tau }{m^{\ast }}=\frac{1}{3{\pi }^2}\frac{e^2}{\hslash }{k}_F^2{\ell }_e$$

$$\sigma ={\rho }^{-1}=G_{0}n<T>$$

$$D=\frac{\mu k_{B}T}{e}$$

$$D_H=\frac{\hslash v_F^2}{k_{B}T}$$

$$\frac{{ϵ}_0}{{ϵ}_{\infty }}=(\frac{{\omega }_L}{{\omega }_T}{)}^2$$

$$\mu k_{B}T\propto {\omega }_{T0}^{-3}\propto ϵ/{\omega }_{T0}$$

Full text

I Introduction

The existence of well-defined quasi-particles is taken for granted in the Boltzmann-Drude picture of electronic transport. In this picture, carriers of charge or energy are scattered after traveling a finite distance. The Mott-Ioffe-Regel(MIR) limit is attained when the mean-free-path of a carrier falls below its Fermi wavelength or the interatomic distanceHussey:2004 . In most metals, resistivity saturates when this limit is approached. But in “bad”Emery:1995 or “strange”Sachdev:2015 metals, it continues to increaseGunnarsson:2003 . It is indeed strange when the mean-free-path persists to fall after attaining its shortest conceivable magnitude and often unexpected behavior is considered bad.

In most cases, bad metals present a linear temperature dependence beyond the MIR limit. Bruin et al.Bruin:2013 recently noticed that the T-linear scattering rate in numerous metals, either ordinary or strange, has a similar magnitude. This observation suggests the relevance of a universal Planck timescale ($\tau_{P}\sim\frac{\hbar}{k_{B}T}$, where $k_{B}$ is the Boltzmann and $\hbar$ the reduced Planck constants) to electronic dissipation and motivated a theoretical attempt to quantify an upper limit to the diffusion constant in incoherent metalsHartnoll:2014 . During the past years, several theories of charge transport with no need for well-defined quasi-particles were proposedMukerjee:2006 ; Lindner:2010 ; Andreev:2011 ; Davison:2014 ; Principi:2015 ; Pakhira:2015 ; Lim:2015 ; Perep:2016 . More recently, direct measurements of thermal diffusivityZhang:2016 have provided additional evidence for quasi-particle-free thermal transport at room temperature in cuprates.

We show here that n-doped SrTiO3 is an unnoticed case of strange or bad metallicity. The resistivity of this dilute metal decreases by orders of magnitude upon cooling to cryogenic temperaturesFredrikse:1964 ; Tufte:1967 ; Fredrikse:1967 ; Wemple:1969 ; Spinelli:2010 . In the low-temperature limit, resistivity follows a T-square behaviorVandermarel:2011 ; Lin:2015 , as expected in a Fermi liquid. Above 100 K, however, the temperature dependence is close to cubicTufte:1967 ; Lin:2015 . In this regime, the mean-free-path of carriers becomes shorter than their wavelength. At room temperature, it falls well below the interatomic distance, the lowest conceivable length scale. Strontium titanate is the strangest known metal according to the criteria for strangeness widely used. Since quasi-particles in this system are not well-defined in a time scale long enough to allow the existence of a scattering time, charge transport cannot be reasonably described by a phonon-scattering picture. This was the approach in previous attemptsFredrikse:1964 ; Tufte:1967 ; Fredrikse:1967 ; Wemple:1969 ; Verma:2014 ; Himmetoglu:2014 ; Zhou:2016 to understand charge transport. We argue that metallicity is caused by the temperature dependence of the transmission coefficient along Landauer canals between dopants. Such a picture does not require a scattering time or a mean-free-path. We find an empirical link between mobility and permittivity, which gives a reasonable account of the experimental data. Providing a quantitative account of this observation emerges as a specific challenge to transport theory.

II Results

II.1 Metallicity beyond the MIR limit in strontium titanate

Fig. 1a shows the temperature dependence of resistivity in SrTiO3-δ as the carrier concentration is changed from 2.4 1017cm*-3* to 3.5 1019cm*-3*. At low temperature ($T\ll 100K$), the system displays a T-square resistivityVandermarel:2011 ; Lin:2015 as expected for electron-electron scatteringPal:2012 in a Fermi liquid. Plotting resistivity as a function of T2 (see Fig. 2 in ref.Lin:2015 ), one can see that inelastic resistivity becomes T-square in the low-temperature limit. A wide range of dense Fermi liquids display Kadowaki-Woods scalingKW of their T-square resistivity prefactor and their electronic specific heat. Since the latter is proportional to carrier concentration, the case of low-density systems such as doped SrTiO3 is differentHussey:2005 . However, the scaling between the resistivity prefactor and Fermi energy persists. Indeed, the magnitude of this prefactor decreases by several orders of magnitude with changing carrier concentrationLin:2015 .

Fig. 1b shows the temperature dependence of the extracted Hall mobility, $\mu=\frac{1}{ne\rho}$. Above 100 K, it displays a temperature dependence close to T*-3* and barely varies with carrier concentration. Our data is in agreement with the less extensive data reported previously by Tufte and ChapmanTufte:1967 . Fig. 1c shows how the exponent of inelastic resistivity evolves as a function of temperature. The total resistivity can be expressed as $\rho=\rho_{0}+AT^{\alpha}$. As seen in Fig. 1c, $\alpha$ is 2 at very low-temperature ($T<50K$) but smoothly rises with warming. One does not expect the T-square resistivity to survive at the Fermi degeneracy temperature. Therefore, the electron-electron scattering origin of the T-square term in the dilute limit has been put into questionMaslov2017 ; Swift2017 . We note, however, that the smooth variation of $\alpha$, makes the detection of the upper boundary of T-square resistivity impossible. As one can see in the figure, $\alpha$ peaks around 150 K at a value slightly exceeding 3 and then decreases with increasing temperature.

In the zero temperature limit, the magnitude of electron mobility, set by defect scattering can become remarkably large in doped strontium titanateSon:2010 . As a consequence, quantum oscillations are easily detectable in moderate magnetic fieldsLin:2013 ; Allen:2013 ; Lin:2014 . The large magnitude of defect-limited mobility at low temperature and its evolution with carrier concentration can be explained in a simple modelBehnia:2015 invoking the long effective Bohr radius of the quantum paraelectricMuller:1979 parent insulator.

The focus of the present paper is charge transport above 100 K where mobility presents a strong temperature dependence and almost no variation with carrier concentration over two orders of magnitude (Fig. 1b). Early studiesFredrikse:1964 ; Tufte:1967 ; Fredrikse:1967 ; Wemple:1969 attributed the T*-3* variation of mobility to the scattering of carriers by phonons. There was a controversy between Fredrikse et al.Fredrikse:1967 (who invoked longitudinal optical phonons) and Wemple et al.Wemple:1969 (who argued in favor of transverse optical phonons). Neither during this early debateFredrikse:1964 ; Tufte:1967 ; Fredrikse:1967 ; Wemple:1969 , nor in more recent theoretical accounts of the temperature dependence of mobility in n-doped SrTiO3Baratoff:1981 ; Verma:2014 ; Himmetoglu:2014 ; Mikheev:2015 ; Zhou:2016 , the magnitude of the mean-free-path was discussed.

In the Drude-Boltzmann picture, the conductivity, $\sigma$, of a metal depends on fundamental constants and a number of material-related properties. These are either, the scattering time $\tau$, and the effective mass, $m^{*}$, or the Fermi wave-vector, kF and the electron mean-free-path, $\ell_{e}$. Namely:

[TABLE]

The Fermi surface of n-doped SrTiO3 in the dilute limit is known. It is located at the center of the Brillouin zone, because a band originating from Ti atoms’ t2g orbitals has a minimum at the $\Gamma-$pointVandermarel:2011 ; Allen:2013 ; Tao:2016 . The threefold degeneracy of this band is lifted by tetragonal distortion and spin-orbit coupling. As the system is doped, the three bands are filled successively and three concentric Fermi surfaces will emerge and grow in size one after the other. This is a picture based on band calculationsVandermarel:2011 and confirmed by experimental studies of quantum oscillationsLin:2013 ; Allen:2013 ; Lin:2014 . Below 1018cm*-3*, the first critical doping for the emergence of secondary pockets, there is a single Fermi surface with moderate (1.6) anisotropyAllen:2013 ; Lin:2014 ; Tao:2016 . Therefore, kF can be quantified in a straightforward manner. Fig. 2a shows the temperature dependence of the mean-free-path extracted from Eq. 1 in a dilute sample whose resistivity was measured up to 400 K. The carrier density is the one given by the Hall coefficient. As previously reported in ref. Tufte:1967 , the Hall coefficient does not display any notable temperature dependence. Moreover, the carrier density according to the magnitude of the Hall coefficient matches the Fermi surface volume according to the frequency of quantum oscillationsLin:2014 . Therefore, there is little ambiguity regarding carrier concentration.

As seen in Fig. 2a, the mean-free-path becomes shorter than the inverse of the Fermi wave-vector k${}_{F}^{-1}$ and then the lattice parameter $a$. Now, at this carrier concentration, with an effective mass of m*∗=1.8me*, the Fermion degeneracy temperature is as low as 15 KLin:2013 . As one sees in the figure, this is the temperature at which de Broglie thermal wavelength, $\Lambda=\frac{h}{\sqrt{2\pi m^{*}k_{B}T}}$ becomes comparable to the interelectron distance $n^{-1/3}$. Above this temperature, the electrons become non-degenerate and follow a Maxwell-Boltzmann distribution. As a consequence and thanks to thermal excitation, the typical carrier momentum is larger than $\hbar$kF. In other words, the typical velocity is not the Fermi velocity, but the thermal velocity, $v_{T}=\sqrt{\frac{2k_{B}T}{m^{*}}}$. Let us define the mean-free-path of electrons with thermal velocity as $\ell^{\prime}_{e}=\tau v_{T}=\ell_{e}n^{-1/3}/\Lambda$. As seen in the figure, because of $\ell^{\prime}_{e}>\ell_{e}$, the crossover temperatures shift upward. However, the picture remains qualitatively the same. In the non-degenerate regime, the relevant wavelength is $\Lambda$ and not the Fermi wavelength. As seen in the figure, the mean-free-path becomes shorter than $\Lambda$ too.

A room-temperature resistivity of 2.4 m$\Omega$.cm implies a scattering time of $\tau\simeq 6fs$. This is shorter than the Planck timeBruin:2013 ($\tau_{P}=\frac{\hbar}{k_{B}T}$) at room temperature, $\tau_{P}(300K)=25.3fs$. This is the typical time it takes for a carrier with a thermal velocity, vT, to move as far as its de Broglie thermal wavelength ( $\frac{\Lambda}{v_{T}}=1.77\tau_{P}$). By all accounts, room-temperature quasi-particles in dilute metallic strontium titanate do not live long enough to qualify for a scattering-based picture.

A color plot of the mean-free-path in the (T, n) plane produced from the data of Fig.1 and Eq. 1 is presented in Fig. 2b. The MIR limit is exceeded in a high-temperature window, widening with the decrease in carrier concentration. The hitherto unnoticed specificity of SrTiO3 is that it becomes a strange metal well below room temperature. The data in Table 1 gives an idea of the “strangeness” or the “badness” of SrTiO3 compared to two other perovskytes. As seen in the table, at 400 K, k${}_{F}\ell$ in this system is much lower than in cuprates or in Sr2RuO4. Contrary to the two other systems, the passage beyond the MIR limit occurs well below room temperature implying the necessity of a transport picture with no reference to well-defined quasi-particles. This is the first principal message of this paper.

II.2 Comparison with graphene and metallic silicon

The temperature dependence of resistivity above 100 K and the magnitude of inelastic resistivity are very different from dilute metallic systems subject to phonon scattering. Let us compare strontium titanate with two exemplary systems. A recent study of charge transport in grapheneEfetov:2010 has shown the relevance of the Bloch-Grüneisen picture of electron-phonon scattering in our temperature window of interest. In this picture, above a characteristic temperature (usually, but not always, the Debye temperature) resistivity displays a linear temperature dependence. This happens because all phonon modes capable of scattering electrons are thermally populated and the phase space for scattering is proportional to the thermal width near the Fermi level. Far below the characteristic temperature, the resistivity is expected to display a much stronger T5 (in 3D) or T4 (in 2D) temperature dependence because the typical wave-vector of the thermally excited phonons becomes smaller with decreasing temperature. As a consequence, the capacity of scattering phonons to decay the momentum flow decays rapidly with temperature. Efetov and KimEfetov:2010 showed that this picture gives a very satisfactory account of inelastic resistivity in graphene as the carrier density is tuned from 1.36 to 10.8 1013cm*-2*. Let us note that in gated graphene, inelastic (that is, temperature-dependent) resistivity is far from dominating the total resistivity. This is seen in Fig. 3a, which compares the temperature-dependence of resistivity in n-doped SrTiO3 and graphene at an identical interelectron distance. As one can see in the figure, resistivity changes by 200 in SrTiO3 and by 1.6 in graphene. Charge conductivity is higher in graphene by a factor of two at low temperature and by two orders of magnitude at room temperature. A comparison with the case of metallic siliconYamanouchi:1967 reveals a similar discrepancy. As one can see in Fig. 3b, cooling phosphorous-doped silicon leads to a modest change in resistivity, much less than what is seen in doped SrTiO3. As a consequence, while at low-temperature, strontium titanate has a significantly higher mobility, the opposite is true at room temperature. In contrast to strontium titanate, in both graphene and silicon, one can use Eq. 1 one to extract a meaningful mean-free-path, which increases by a factor of two or less as the system is cooled down from room temperature to helium liquefaction temperature.

It is also instructive to compare SrTiO3 with two other dilute metals close to a ferroelectric instability. As one can see in Fig.3c, both PbTe and KTaO3 show comparably large changes in their resistivity upon cooling. Reports on KTaO3Wemple:1965 ; Wemple:1969 and on lead chalcogenide salts (PbTe, PbSe and PbS)Petritz:1955 ; Allagier:1958 indicate that high-temperature mobility does not vary with carrier concentration, but shows a strong temperature dependence ($\mu\propto T^{-\lambda}$, with $\lambda\simeq 2.5-3$). Both these features are similar to what we see in strontium titanate. Only in strontium titanate, however, the magnitude of the room temperature mobility is low enough to make it a clearly strange metal below room temperature.

To sum up, in silicon and graphene, the temperature-induced change in resistivity implies a modest change in mean-free-path and follows a Bloch-Gruneisen behavior (a slow T-linear behavior at high temperature and a fast T4 or T5 behavior at low temperature). On the other hand, doped SrTiO3 and other metals close to a ferroelectric instability do not fit within this picture. The apparent mean-free-path of carriers changes by orders of magnitude. It becomes very short at high temperature, and in the case of strontium titanate, too short to be physically meaningful.

III Discussion

III.1 Conduction as transmission in a doped polar semiconductor

Fig. 4 sketches two alternative descriptions of charge conduction. In the semi-classic picture of metallic charge transport (Fig. 4a), conductivity increases with decreasing temperature, because the scattering events relaxing the momentum of a charge-carrying quasi-particle become less frequent with decreasing temperature. Now, consider an alternative picture (Fig. 4b), where each dopant is hosting a polaron, ‘an electron trapped by digging its own hole’Mott:1940 in a polar semiconductor. The polaron picture has been frequently invoked in the case of strontium titanateEagles:1965 ; Mechelen:2008 .

In this second picture, conductivity is set by transmission among dopant sites and there is no need for well-defined quasi-particles. Can conductivity increase with decreasing temperature in such a picture and generate a metallic behavior? This can happen if cooling increases the transmission probability between adjacent dopant sites. In the case of strontium titanate, static permittivity increases with coolingMuller:1979 . Therefore, the lower the temperature, the shallower the donor potential. As a consequence, polarons become less bound with decreasing temperature and conductivity is metallic.

Let us now consider different length scales of the system. Fig. 5a shows them in our temperature range of interest where mobility becomes independent of carrier concentration. When carrier density changes from $2.4\times 10^{17}cm^{-3}$ to $1.7\times 10^{19}cm^{-3}$, the distance between electrons varies between 16 to 4 nm. Taking the low-temperature effective mass of m*∗=1.8me* seen by quantum oscillationsLin:2013 , one finds that the de Broglie thermal wave-length is $\Lambda\simeq 3-6nm$ in this temperature range. Thus, the system is mostly non-degenerate. Electric permittivity, $\epsilon$, is large ($\epsilon(300K)\simeq 300)$Muller:1979 ; Lowndes:1973 and increases steadily with cooling. As a consequence, the effective Bohr radius (a${}^{*}_{B}=\frac{4\pi\epsilon\hbar^{2}}{m^{*}e^{2}}$) varies between 8 and 40 nm. This puts the system above the Mott criterion for metallicity (n1/3 a${}^{*}_{B}>0.25$Edwards:1978 ), which, one shall not forget, is relevant to degenerate electronsMott:1990 . These length scales are in the same range of magnitude. They are all longer than the lattice parameter (0.39nm). The question is how to picture conduction as transmissionImry:1999 along a random network of donors.

Since mobility is found to be independent of carrier concentration above 100K, we can express conductivity as:

[TABLE]

Here, $G_{0}=\frac{2e^{2}}{h}$, is the quantum of conductance and $<T>$ represents the average transmission between a dopant site and its immediate neighbors. Note that in three dimensions, $<T>$ is proportional to mobility ($\mu=2\frac{e}{h}<T>$).

The temperature dependence of $<T>$, extracted from the experimental data using Eq. 2 is shown in Fig. 5b. As seen in the figure, a hundred-fold enhancement in carrier concentration does not affect $<T>$. One would have expected that the Landauer transmission between one site and its more or less distant neighbors would depend on the length of the trajectory and the details of the structural landscape. It is therefore surprising that the averaged transmission coefficient, $<T>$, is insensitive to such a large change in the average interdopant distance.

Fig. 5b also compares the magnitude of $<T>$ with $\Lambda^{2}$. the latter represents the areal uncertainty in the spatial localisation of a non-degenerate electron in three dimensions. As seen in the figure, $<T>$ decreases faster than $\Lambda^{2}$. There is little experimental information regarding the effective mass in this temperature range. A larger temperature-dependent effective mass would make $\Lambda^{2}$ smaller and its decrease faster. Thus, one can bridge the gap between $<T>$ and $\Lambda^{2}$ with a hypothetical temperature-dependent polaronic mass. However, there is no experimental evidence for this. At low temperatures, quantum oscillationsLin:2014 ; Allen:2013 resolve a modest mass enhancement($\leq 4$). This is also the case of infrared conductivityMechelen:2008 . Thus, we cannot simply picture conductivity as ballistic charge transport along Landauer wires. Let us now consider a diffusive picture.

III.2 Mobility, diffusivity and their link to electric permittivity

In a non-degenerate semiconductor, mobility and diffusion constant, $D$, of carriers are linked through Einstein’s equationAshcroft:1976 :

[TABLE]

The temperature dependence of $D$ extracted from the mobility data of the sample with a carrier concentration of 2.4 1017 cm*-3* is shown in Fig. 6a. Note that since mobility does not show any detectable variation with carrier concentration, this curve is representative of $D$ for carrier concentrations in the range of 1017-1019cm*-3*. The magnitude of $D$ obtained in this way is remarkably low, well below 1cm2/s. For comparison, the diffusion constant of electrons in silicon rises from 35 cm2/s at room temperature to $\sim$100 cm2/s at 100 KBrunetti:1981 .

Hartnoll recently proposed a lower bound to diffusion constant in incoherent metalsHartnoll:2014 :

[TABLE]

As one can see in Fig. 6a, the experimental $D$ decreases faster than T*-1*. Hartnoll boundary was obtained for degenerate systems. Ours is non-degenerate and the typical velocity is thermal velocity and not vF. The Fermi velocity changes drastically with carrier density, but the experimental $D$ does not. As defined in Eq. 4 $,D_{H}$, does not appear to be directly relevant to our observation.

An obvious piece of the puzzle of charge transport in strontium titanate is the fact that the insulating parent is a quantum paraelectric with a strongly temperature-dependent electric permittivityLowndes:1973 ; Muller:1979 . We have found that in our temperature range of interest $D$ is proportional to $\epsilon^{1.5}$. This empirical observation is the second principal message of this paper.

The scaling between static electric permittivity, $\epsilon_{0}$, and the frequency of the Transverse Optic (TO) soft modeFleury:1968 ; Yamada:1969 , $\omega_{TO}$ in strontium titanate is well-known. Yamada and ShiraneYamada:1969 showed that $\omega_{TO}=194.4\sqrt{\epsilon^{-1}}$ within experimental resolution. In a polar crystal, there is a theoretical link between the ratio of static, $\epsilon_{0}$, to high-frequency, $\epsilon_{\infty}$, permittivity and the ratio of longitudinal, $\omega_{L}$, to transverse, $\omega_{T}$, phonon frequencies. This is the expression first derived by Lyddane, Sachs, and TellerLyddane:1941 ; Cohran:1962 :

[TABLE]

When the transverse mode is soft, the system begins to show a large static polarizability. As one can see in Fig. 6b, the available experimental data confirm the scaling between these two distinct measurable quantities. A theory assuming an anisotropy in the polarizability of the oxygen ionMigoni:1976 , the starting point of the polarization theory of ferroelectricityBilz:1987 , explains the temperature dependence of $\omega_{TO}$ in strontium titanate quantitatively. The soft mode and the large permittivity are properties of the insulating parent. However, they are known to survive in presence of dilute metallicity. Indeed, neutron scattering studies have explored the way the soft mode responds to the introduction of mobile electronsBauerle ; Bussmann:1981 and found negligible shift in frequency for carrier densities below 7.8 1019cm*-3*.

As one can see in Fig. 6a, comparing our data with those reported by Yamada and ShiraneYamada:1969 , one finds that:

[TABLE]

An explanation for this empirical link between carrier mobility and lattice properties is beyond the scope of this paper and emerges as a challenge to theory.

III.3 Concluding remarks

The persistence of T-square resistivity in dilute metallic strontium titanate is puzzlingLin:2015 . However, its context is familiar. Electrons are degenerate and k${}_{F}\ell>>1$. We now see that this low-temperature puzzle is only the tip of an iceberg. Above 100 K, the application of the Drude picture of conductivity yields a paradox: a carrier mean-free-path shorter than all conceivable length scales. Both the magnitude and the functional behavior of the temperature-induced change in resistivity are very different from what is expected according to the Bloch-Grüneisen law and what is seen in silicon and graphene. The aim of this paper is to attract theoretical attention to a hitherto unnoticed case of strange metallicity. It remains to be seen if electron viscosity plays any role in diffusive transport. On the experimental side, extending the available data to higher temperatures and lower doping concentration would map the boundaries of metallicity and the MIR limit in this system as well as other polar semiconductors.

It is a pleasure to thank Sean Hartnoll and Dmitrii Maslov for stimulating discussions. This work has been supported by an Ile de France regional grant, by Fonds ESPCI-Paris and by JEIP- Collège de France and funded in part by a QuantEmX grant from ICAM and the Gordon and Betty Moore Foundation through Grant GBMF5305 to KB.