Unusual non saturating Giant Magneto-resistance in single crystalline Bi2Te3 topological insulator

TL;DR

This study synthesizes high-quality Bi2Te3 single crystals and demonstrates their large, non-saturating magnetoresistance at low temperatures, which persists up to room temperature, highlighting an intrinsic property of the bulk material.

Contribution

It reports the synthesis and detailed characterization of Bi2Te3 crystals showing unprecedented non-saturating giant magnetoresistance at low temperatures.

Findings

250% magnetoresistance at 2.5K under 50KOe

Non-saturating MR persists up to room temperature

Intrinsic bulk property, not size-effect related

Abstract

We report synthesis, structural details and electrical transport properties of topological insulator Bi2Te3. The single crystalline specimens of Bi2Te3 are obtained from high temperature (950C) melt and slow cooling (2C/hour). The resultant crystals were shiny, one piece (few cm) and of bright silver color. The Bi2Te3 crystal is found to be perfect with clear [00l] alignment. The powder XRD pattern being carried out on crushed crystals showed that Bi2Te3 crystallized in R3m symmetry with a = b = 4.3866(2) A, c = 30.4978(13) A and Gamma = 120degree. The Bi position is refined to (0, 0, 0.4038 (9)) at Wyckoff position 6c and of Te are (0, 0, 0) at Wyckoff position 3a and at (0, 0, 0.2039(8)) at 6c. Ambient pressure and low temperature (down to 2K) electrical transport measurements revealed metallic behavior. Magneto transport measurements under magnetic field showed huge non saturating magneto resistance (MR) reaching up to 250% at 2.5K and under 50KOe field. Summarily, the short communication clearly demonstrates that Bi2Te3 topological insulator exhibit non-saturating large positive MR at low temperature of say below 10K. The non saturating MR is seen right up to room temperature albeit with much decreased magnitude. Worth mentioning is the fact that these crystals are bulk in nature and hence the anomalous MR is clearly an intrinsic property and not due to the size effect as reported for nano-wires or thin films of the same.