Oxygen non-stoichiometry and the origin of Na ion ordering in P2-NaxCoO2

TL;DR

This study explores how oxygen vacancies influence sodium ion ordering in Na_xCoO2, revealing that oxygen deficiency stabilizes superlattice structures and affects the material's magnetic and transport properties.

Contribution

It demonstrates that oxygen vacancies are crucial in stabilizing Na ion superlattice ordering in Na_xCoO2, linking oxygen deficiency to structural and property changes.

Findings

Oxygen vacancies stabilize superlattice structures.

Na2/3CoO1.98 exhibits similar properties to Na0.71CoO2.

Na ion ordering is influenced by oxygen defects.

Abstract

The impact of oxygen deficiency on physical properties of Na2/3CoO2-x has been investigated. From the combined thermogravimetric, magnetic susceptibility and synchrotron X-ray Laue diffraction studies, it is demonstrated that Na2/3CoO2 shows no superlattice ordering due to Na ions; however Na2/3CoO1.98, which has the same Co valence as that of Na0.71CoO2, shows nearly identical magnetic and transport properties and the same simple hexagonal superlattice ordering of sqrt(12)a. It is proposed that the Na ion ordering found in Na2/3CoO1.98 is identical to the ideal Na0.71CoO2 of large sqrt(12)a x sqrt(12)a x 3c superlattice but with additional Na vacancies which are bound to the oxygen defects at room temperature. We conclude that oxygen vacancies play a key role in stabilizing the superlattice structure and must be accounted for in its modeling.