Structural Basis for the Anomalously Low Spontaneous Polarisation Values of the Polar Phase of Sr1-xCaxTiO3 (x=0.02, 0.04): Evidence for a Ferrielectric Ordering

TL;DR

This study investigates the crystal structure and phase transitions of Sr1-xCaxTiO3, revealing ferrielectric ordering that explains its unusually low spontaneous polarization values through detailed diffraction analysis.

Contribution

It provides the first detailed structural evidence for ferrielectric ordering in Sr1-xCaxTiO3, linking microscopic displacements to low polarization.

Findings

Identified phase transitions at 170 K and ~32 K via x-ray diffraction.

Discovered off-centre displacements of ions in the polar phase.

Demonstrated ferrielectric coupling causes low spontaneous polarization.

Abstract

Full pattern Le-Bail refinement using x-ray powder diffraction profiles of Sr1-xCaxTiO3 for x=0.02, 0.04 in the temperature range 12 to 300 K reveals anomalies in the unit cell parameters at 170, 225 K due to an antiferrodistortive (cubic to tetragonal I4/mcm) phase transition and at ~32, ~34 K due to a transition to a polar phase (tetragonal I4/mcm to orthorhombic Ic2m), respectively. The lower transition temperatures obtained by us are in excellent agreement with those reported on the basis of the dielectric studies by Bednorz and Muller, [10] who attributed these to ferroelectric transition. Rietveld analysis of the diffraction profiles of the polar phase reveals off-centre displacements of both Sr2+/Ca2+ and Ti4+ ions in the X-Y plane along <110> pseudocubic directions, in agreement with the experimentally reported direction of easy polarization by Bednorz and Muller, but the resulting dipole moments are shown to be ferrielectrically coupled in the neighbouring (001) planes along the [001] direction leading to anomalously low values of the spontaneous polarization at 12K.